U0805CxxxxxT PDF 데이터시트 : 부품 기능 및 핀배열

부품번호 U0805CxxxxxT
기능 Multilayer Ceramic Capacitors
제조업체 Multicomp
로고 Multicomp 로고 


전체 19 페이지

		

No Preview Available !

U0805CxxxxxT 데이터시트, 핀배열, 회로
www.DataSheet4U.com
Nickel Barrier
Multilayer Ceramic Capacitors
Features:
Multilayer ceramic chip capacitor.
Nickel barrier termination.
High performance and reliability.
0603, 0805, and 1206 case size.
Rated Voltage
Code
Rated Voltage
A
B
T
U
Part Dimension
100
16
25
50
Length
(L)
1.6 ±0.1
2.0 ±0.2
3.2 ±0.2
Width
(W)
Maximum
Thickness
(T)
0.8 ±0.1
1.25 ±0.1
1.40
1.60 ±0.2
1.52
Dimensions
Minimum
MB
0.20
0.25
Minimum
G
0.40
0.70
1.40
Voltage
(V)
6.3 ~ 50
6.3 ~ 500
6.3 ~ 1000
Type
0603
0805
1206
Page 1
27/04/06 V1.0




U0805CxxxxxT pdf, 반도체, 판매, 대치품
www.DataSheet4U.com
Nickel Barrier
Multilayer Ceramic Capacitors
Performance
Item
External
Appearance
Voltage Proof
Performance
Test or Inspection Method
No defects which may affect
performance
Visual inspection and dimension measurement
DC Tested voltage shall be applied for 1 ~ 5 second.
Charge/discharge current shall not exceed 50mA (PS : Ra
- Rated Voltage)
Withstand test voltage without insulation
breakdown or other damage
Code
200V
250V
500V/630V
1KV
Temperature Coefficient
NPO
1.5Ra
X7R/X5R
2.5Ra
2.0Ra
1.5Ra
1.25Ra
Y5V
-
Insulation Resistance
Capacitance
(Cap.)
Dissipation Factor (D.F)
NPO:
100,000Mminimum or R x C 1000x
F (Which ever is smaller)
X7R, X5R, Y5V, Z5U:
10,000Mminimum or R x C 1000x
F (Which ever is smaller)
Rated Voltage
DC Tested Voltage
<1KV
1.0 Ra
1KV
1KV
Apply DC tested voltage for 60 ±5 minute.
(PS : Ra - Rated Voltage)
Within the specified tolerance
NPO:
30pF: Q 1000
<30pF: Q 400 + 20C
PS:C: Nominal Capacitance (pF)
X7R, X5R, Y5V, and Z5U : (Maximum
Value)
T.C.
X7R/
X5R
Z5U
50V
25V
16V 10V
2.5% 3.0% 3.5% 5.0%
4.0% - - -
Measuring Frequency:
Z5U,Y5V, X7R, X5R : 1KHz ±50Hz
NPO:
>1000pF:1KHz ±50Hz.
1000pF:1MHz 100KHz.
Measuring Voltage:
Z5U:0.5Vrms.
NPO:
X7R, X5R, Y5V:1.0 ±0.2Vrms.
Y5V 5.0% 7.5% 9.0% 12.5%
Page 4
27/04/06 V1.0

4페이지










U0805CxxxxxT 전자부품, 판매, 대치품
www.DataSheet4U.com
Nickel Barrier
Multilayer Ceramic Capacitors
Item
Performance
Vibration
External
Appearance
Without distinct Damage
Capacitance
Change
(C/C)
NPO: ±2.5% or ±0.25 pF maximum
(Whichever is larger)
X7R/X5R: ±7.5%
Y5V, Z5U: ±20%
NPO: C 30pF : Q 1000
C<30pF:Q 400 + 20°C
PS: C : Nominal capacitance (pF)
X7R, X5R, Y5V, Z5U : (Maximum Value)
DF or Q
T.C.
X7R/
X5R
Z5U
50V
25V
16V 10V
2.5% 3.0% 3.5% 5.0%
4.0% - - -
Y5V 5.0% 7.5% 9.0% 12.5%
External
Appearance
No mechanical Damage
Deflection
Bending
Strength
Capacitance
Change
(C/C)
Flexure 1mm
NPO: ±5% or ±0.5 pF maximum
(Whichever is larger)
X7R/X5R: ±12.5%
Y5V: ±30%
Test or Inspection Method
(Not apply for 0402 product)
Solder the capacitors to the test jig as shown in figure below
with IR-Reflow method. The capacitor shall be subjected to a
simple harmonic motion with the entire frequency range, from
10 to 55 Hz and return to 10 Hz ,shall be transverse in 1 min.
Amplitude (total excursion): 1.5mm
Amplitude tolerance: ± 15%
This motion shall be applied for a period of 2
hours in each of 3 mutually perpendicular
directions (a total of 6 hours)
External
Appearance
No mechanical Damage
Capacitance
Change
(C/C)
DF
NPO: ±2.5% or ±0.25 pF maximum
(Whichever is larger)
X7R/X5R: ±7.5%
Y5V: ±20%
NPO: C 30pF : Q 1000
C<30pF: Q 400 + 20°C
Temperature
Cycle
X7R, X5R, Y5V and Z5U (Maximum value)
T.C.
X7R/
X5R
50V
25V
16V 10V
2.5% 3.0% 3.5% 5.0%
(Not apply for 0402 product)
The capacitor shall be subject 5 cycles according to four heat
treatments listed in the following table.
Then leave the capacitors in ambient condition for the
following time before measurement.
Class II: 2~24 hours
Step
Temperature (°C)
Duration
(Minutes)
1 Minimum Operation Temperature ±3 30 ±3
2 Room Temperature (25°C)
2~5
3 Minimum Operation Temperature ±3 30 ±3
4 Room Temperature (25°C)
2~5
Z5U 4.0% - - -
Y5V 5.0% 7.5% 9.0% 12.5% Preconditioning: (only for class 2):
Perform a heat treatment at 150+0-10°C for one hour and
IR
1000Mminimum or 50*F
(Whichever is smaller)
then let sit for 24 ±2 hours at room temperature.
Perform initial measurement.
Page 7
27/04/06 V1.0

7페이지



구       성총 19 페이지
다운로드[ U0805CxxxxxT.PDF 데이터시트 ]
구매 문의
일반 IC 문의 : 샘플 및 소량 구매
-----------------------------------------------------------------------

전력 반도체 판매 ( IGBT, TR 모듈, SCR, 다이오드 모듈 )

휴대전화 : 010-3582-2743


상호 : 아이지 인터내셔날

전화번호 : 051-319-2877, [ 홈페이지 ]



링크공유

링크 :

관련 데이터시트

부품번호상세설명 및 기능제조사
U0805CxxxxxT

Multilayer Ceramic Capacitors

Multicomp
Multicomp

추천 데이터시트

부품번호상세설명 및 기능제조사
CQ1565RT

FSCQ1565RT, Green Mode Fairchild Power Switch. In general, a Quasi-Resonant Converter (QRC) shows lower EMI and higher power conversion efficiency compared to conventional hard-switched converter with a fixed switching frequency.

Fairchild
Fairchild
KF16N25D

MOSFET의 기능은 N Channel MOS Field effect transistor입니다. This planar stripe MOSFET has better characteristics, such as fast switching time, low on resistance, low gate charge and excellent avalanche characteristics. It is mainly suitable for DC/DC Converters and switching mode power supplies.( Vdss=250V, Id=13A )

KEC
KEC

DataSheet.kr    |   2018   |  연락처   |  링크모음   |   검색  |   사이트맵